Main Title: Präparation von poröser calciumphosphat-basierter Biokeramik für die Implantologie und das Tissue Engineering
Translated Title: Preparation of porous calcium phosphate based bioceramics for implantology and tissue engineering.
Author(s): Hitzegrad, Frank
Advisor(s): Fleck, Claudia
Granting Institution: Technische Universität Berlin, Fakultät III - Prozesswissenschaften
Type: Doctoral Thesis
Language: German
Language Code: de
Abstract: Die vorliegende Arbeit zum Thema „Präparation von poröser calciumphosphat-basierter Biokeramik für die Implantologie und das Tissue Engineering“ soll einen Beitrag zur Herstellung von offenporiger, calciumorthophosphat-haltiger Keramik und deren Charakterisierung leisten. Es wurden calciumphosphat-basierte Pulver präpariert, daraus poröse Biokeramiken hergestellt und diese charakterisiert. Das generelle Arbeitsziel war die Präparation von biokeramischen Pulvern von zwei erst in jüngster Zeit dargestellten, resorbierbaren Calciumorthophosphaten. Die verwendeten Werkstoffe waren zum einen Ca2KNa(PO4)2 (Ca2, neuwertiger Werkstoff) und zum anderen Ca10[K/Na](PO4)7 (Ca10, neuartiger Werkstoff) als Hauptkristallphase. Ein weiteres Arbeitsziel war die Präparation von zwei langzeitstabilen überwiegend calciumorthophosphat-basierten Werkstoffen, zum Einen mit Ca10(PO4)6(F)2 und CaSiO3 (Ap40STE) sowie zum Anderen mit Ca10(PO4)6(F)2 und CaZr4(PO4)6 (FA-CZP, neuartiger Werkstoff). Die Herstellung von Prüfkörpern erfolgte überwiegend nach dem „Schwartzwalder-Somers-Verfahren“. Dafür wurden die relevanten Kenndaten ermittelt. Außerdem erfolgte eine Charakterisierung der erhaltenen Schwammkeramiken, um die Eigenschaften in Abhängigkeit von der Morphologie zu bestimmen. Durch die Herstellung von Schwammkeramiken aus synthetisierten Werkstoffen war es möglich, ein offenporiges, mechanisch stabiles Füllmaterial für Knochendefekte mit durchgängigen Poren und trabekelartigen Stegen zu generieren.
The present work on the theme „Preparation of porous calcium phosphate based bioceramics for implantology and tissue engineering“, is to contribute to preparation of porous calcium phosphate based ceramics and their characterization. The general target of this thesis was the preparation of bioceramic powders of two resorbable Calcium salts of orthophosphoric acids developed most recently. The materials used were the Ca2KNa(PO4)2 (Ca2, new material) and the Ca10[K/Na](PO4)7 (Ca10, new material) as a main crystal phase. A further goal was the preparation of two mainly long-term stable calcium orthophosphate, the Ca10(PO4)6(F)2 and CaSiO3 (Ap40STE) as well as the Ca10(PO4)6(F)2 and CaZr4(PO4)6 (FA-CZP, new material). The productions of test specimens were mainly made in accordance to the procedure developed by Schwartzwalder and Somers. For this reason the relevant database were determined. In addition, all ceramic foams were characterized depending on the properties of the morphology. By the preparation of ceramic foams from synthesized materials, it was possible to generate a open-cell, mechanically stable filling material for bone repair with interconnected pores and struts like Trabecular.
URI: urn:nbn:de:kobv:83-opus-22560
http://depositonce.tu-berlin.de/handle/11303/2467
http://dx.doi.org/10.14279/depositonce-2170
Exam Date: 12-Dec-2008
Issue Date: 11-Jun-2009
Date Available: 11-Jun-2009
DDC Class: 500 Naturwissenschaften und Mathematik
Subject(s): Biokeramik
Calciumphosphate
Knochenersatz
Porosität
Tissue Engineering
Bioceramics
Bone replacement
Calcium phosphate
Porosity
Tissue Engineering
Usage rights: Terms of German Copyright Law
Appears in Collections:Technische Universität Berlin » Fakultäten & Zentralinstitute » Fakultät 3 Prozesswissenschaften » Institut für Werkstoffwissenschaften und -technologien » Publications

Files in This Item:
File Description SizeFormat 
Dokument_50.pdf13.73 MBAdobe PDFThumbnail
View/Open


Items in DepositOnce are protected by copyright, with all rights reserved, unless otherwise indicated.